Effect of low-temperature precipitation on the transformation characteristics of Ni-rich NiTi shape memory alloys during thermal cycling
M. F.-X. Wagner, S. R. Dey, H. Gugel, J. Frenzel, C. Somsen, G. Eggeler.
Intermetallics, 18, 1172-1179, (2010)
Thermal cycling of NiTi shape memory alloys is associated with functional fatigue: the characteristic phase transformation temperatures decrease with increasing number of cycles, and the transformation behavior changes from a single- to a two-stage martensitic transformation involving the intermediate R-phase. These effects are usually attributed to a gradual increase of dislocation density associated with micro-plasticity during repeated cycling through the transformation range. Here, these changes are shown to increase at a higher maximum temperature (in the fully austenitic state) during differential scanning calorimetric cycling of a Ni-rich alloy. Additional thermal cycling experiments without repeated phase transformations, and post-mortem microstructural observations by transmission electron microscopy, demonstrate that a relevant portion of functional fatigue is due to the formation of nano-scale Ni-rich precipitates of type Ni4Ti3 even at temperatures relatively close to the austenite finish temperature. These results show that both dislocation generation during the diffusion-less phase transformation, and diffusion-controlled nucleation and growth of Ni4Ti3 precipitates, can interact and contribute to the evolution of functional properties during thermal cycling of Ni-rich NiTi.