On the influence of alloy composition on creep behavior of Ni-Based single-crystal superalloys (SXs)

O. M. Horst, A. Ibrahimkhel, J. Streitberger, N. Wochmjakow, P. Git, F. Scholz, P. Thome, R. F. Singer, C. Körner, J. Frenzel, G. Eggeler.

Superalloys 2020, Springer, Cham, 60-70, (2020)

In the present work, three Ni-based single-crystal superalloys (SXs) were investigated, a Re-containing alloy ERBO/1 (CMSX-4 type) and two Re-free SXs referred to as ERBO/15 and ERBO/15-W, which differ in W content. The microstructural evolution of the three alloys during heat treatment and their creep behavior is investigated. When one applies one heat treatment to all three alloys, one obtains different γ/γ′-microstructures. Subjecting these three alloys to creep in the high-temperature low-stress creep regime, ERBO/15 outperforms ERBO/1. In order to separate the effects of alloy chemistry and microstructure, the kinetics of the microstructural evolution of the three alloys was measured. The results were used to establish similar microstructures in all three alloys. Comparing ERBO/15 with ERBO/15-W, it was found that in ERBO/15-W particles grow faster during the first precipitation heat treatment and that ERBO/15-W creeps significantly faster. At constant microstructures, ERBO/15 and ERBO/1 show similar creep behavior. In the high-temperature and low-stress creep regime, ERBO/15 shows lower minimum creep rates but ERBO/1 features a slower increase of creep rate in the tertiary creep regime. It was also found that in the high-temperature low-stress creep regime, ERBO/1 shows a double minimum creep behavior when particles are small.

Keyword(s): creep; γ/γ′-microstructure; alloy chemistry; Re and Re-free superalloy single crystals
Cite as: https://link.springer.com/chapter/10.1007%2F978-3-030-51834-9_6
DOI: 10.1007/978-3-030-51834-9_6