Ruddlesden–Popper oxyfluorides of the substitution series La2Ni1–xCuxO3F2 (0 ≤ x ≤ 1) were obtained by topochemical fluorination with polyvinylidene fluoride (PVDF) of oxide precursors La2Ni1–xCuxO4. The thermal stability and the temperature-dependent unit cell evolution of the oxyfluorides were investigated by high-temperature XRD measurements. The oxyfluoride with x = 0.6 shows the highest decomposition temperature of θdec ∼ 520 °C, which is significantly higher than the ones found for the end members La2NiO3F2 (x = 0) θdec ∼ 460 °C and La2CuO3F2 (x = 1) θdec ∼ 430 °C. The magnetic properties of all La2Ni1–xCuxO3F2 oxyfluorides were characterized by field- and temperature-dependent measurements as well as DFT calculations of the magnetic ground state. An antiferromagnetic ordering was derived for all substitution levels. For the Néel temperature (TN), a nonlinear dependence on the copper content was found, and comparably high values of TN in the region of 200–250 K were observed in the broad composition range of 0.3 ≤ x ≤ 0.8.